| Name︰ | polyester（the solor energy）outdoor powder coatings |
| Model No.︰ | 錘紋-1 |
| Brand Name︰ | FLY |
| Export Markets︰ | Application:Household electrical appliances.sands chairs,construction |
| Pricing︰ | RMB:20-24YUAN/KG |
| Min Order︰ | 100KG |
|
|
|
FuLai thermosetting powder coatings based on saturated polyester resins,hardenersand pigments.Formulated for weather ,heat and light resistance
◆General Product Description
◇Density:between1.4-1.8(depending on colour and formulation)
◇Granulometry:depending on application(average)
(particle size)◇<16microns:15%±5%◇16-64microns:75%±5% ◇>64microns:10%±5%
◇volatile:≤1.0% ◇melting range:65-90℃
◇Package:20Kgs in dry conditions at a temperature below 30℃
◇Application:Household electrical appliances.sands chairs,construction
materials,auto mobile parts,mechanical parts,railings .Salor energy with requests on
weather resistance.
◆Application equipment:Epoxy powder coatings can be applied by: High
-tension electrostatic spray’Tribo or friction charged spray;Electorstatic fluidized bed;Fluididsed bed
◆Coverage:Film thickness is between 50-150microns depending on indrstrial requirement.Coverage is between 11-13M/Kg (60microns) depending on colour and type.
◆Stoving conditions:
◇Normal cure:Stoving 15minutes at 180℃;Stoving 10minutes at 200
◇Low Cure:Stoving 15minutes at 160℃
Aspect;Gloss is measured on a 60angle meter in accordance with GB/T 1743-79(89)
Gloss High Gloss(AMP) ≥86%
Semi-gloss 70%-85%
Low-gloss(NMP) Follow request
Effects:Smooth finish Texture-various Specials or request
◆Mechanical performance:All tests csrried out on degreased and zinc phosphated test panels.Prepared under laboratory conditions at a film thinkness of 60-80microns
◇Hardness(Pencil):H-2H GB/T6739-1996
◇Adhesion:Class”0-1” GB/T9286-88
◇Bend test:≤6mm GB/T6742-86
◇Imapact test:50Kgcm GB/T1732-93
◆Corrosion resistance:All tests carried out on degreased and zinc phosphated test panel.Prepared under laboratory conditions at a film thickness of 100-120 microns.
◇Salt spray resistance:400hrs ;less than class 1;GB/T1771-91
◇Humidity resistance:1.000Hrs.Less than class1; GB /T1740-79 (89)
◆Chemical resistance:All tests carried out on degreased and zinc phosphated test panel.Prepared under laboratory conditions at a film thickness of 100-120 microns
Acid Acetic Acid Solution20% Showing no effect after 12months
Sulphuric Acid Solution30% Showing no effect after 12months
Phosphoric Acid Solution30% Showing no effect after 12months
Soda Solution10% Showing no effect after 12months
Bases Amjonia Solution10% Showing no effect after 12months
|
|
|
|
|
|
|
|
|
|
|